Most modern cements contain various additives which improve the properties of both the binders and concrete mixes and concrete. One of the main purposes of their use is the tendency to accelerate the processes of formation of structure and, thereby, increase the cement stone strength at an early age (the age of 1, 3 and 7 days), it is undoubtedly important for builders and manufacturers of precast concrete, as thus reducing time to achieve its demoulding and handling strength. As a result of experimental studies found that Portland cement modification is very small amount of fine carbon-black (up to 0.01 % by weight of cement) of the cement stone can increase the compressive strength at an early age by 18 ÷ 79 %. In this case, the optimal additive is 0.006 mass% of carbon black.
cement stone, nano-sized particles, strength at an early age, fine supplements, carbon-black, specific surface area.
1. Nguyễn Thị Hoàn. Khảo sát vai trò của hạt nano Carbon tới một số các tính chất của xi măng Pooclăng, Đồ án tốt nghiệp, Đại học Bách khoa Hà Nội, 2013, Tr 89. [Nguen Tkhi Khoan. Vliyanie nanorazmernykh chastits ugleroda na svoystva portlandtsementa. Khanoyskiy politekhnicheskiy universitet. 2013, 89 s.].
2. Nguyễn Quang Tùng. Khảo sát khả năng sử dụng phụ gia để tăng cường độ tuổi sớm cho đá xi măng Pooclăng hỗn hợp, Đồ án tốt nghiệp, Đại học Bách khoa Hà Nội, 2013, Tr 91. [Nguen Kuang Tung. Vozmozhnost´ primeneniya mineral´nykh dobavok dlya povysheniya prochnosti portlandtsementnogo kamnya v rannem vozraste. Khanoyskiy politekhnicheskiy universitet. 2013, 91 s.].
3. Vũ Đức Trung, Đào Văn Anh. Khảo sát ảnh hưởng của đá vôi mịn, muội carbon, DEG và TEA tới một số tính chất của xi măng Quang Sơn, Đồ án tốt nghiệp, Đại học Bách Khoa Hà Nội, 2012, Tr 87. [Vu Duk Chung, Van An´ Dao. Issledovanie vliyaniya dobavleniya izvestnyaka i uglerodnoy sazhi na svoystva tsementa «Kuang Son» s pomoshch´yu metoda differentsial´nogo termicheskogo analiza (DEG i TEA). Khanoyskiy politekhnicheskiy universitet. 2012, 87 s.].
4. Bazhenov Yu.M. Sovremennaya tekhnologiya betona //Sovmestnyy mezhdunarodnyy nauchnyy simpozium «Nauchnye dostizheniya v issledovaniyakh o novykh sovremennykh stroitel´nykh mate-rialakh». Khanoy. 2006. C. 12-18.
5. Bazhenov Yu.M., Nguen Din´ Chin´, Nguen Tkhe Vin´. Vysokoprochnye betony s kompleksnym primeneniem zoly risovoy shelukhi, zoly-unosa i superplastifikatorov. Vestnik MGSU. 2012. №1. S. 77–82.
6. Phạm Hữu Hanh. Bê tông cường độ cao- Bê tông chất lượng cao. Trường Đại học Xây dựng- Hà Nội. 2009, tr.80. [Fam Khyu Khan´. Vysokoprochnye i vysokokachestvennye betony //Stroitel´nyy universitet. Khanoy. 2009, 80 c.].
7. Bazhenov Yu.M., Dem´yanova V.S., Kalashnikov V.I. Modifitsirovannye vysokokachestvennye betony. M.: Izd. ASV. 2006, 370 s.
8. Bazhenov Yu.M. Ispol´zovanie nanosi-stem v stroitel´nom materialovedenii //Voprosy primeneniya nanotekhnologiy v stroitel´stve: Sb. dokladov uchastnikov kruglogo stola. M.: MGSU. 2009. C. 4–8.
9. Aleksashin S.V., Bulgakov B.I. Melko-zernistyy beton dlya gidrotekhnicheskogo stroitel´stva, modifitsirovannyy kompleksnoy organomineral´noy dobavkoy //Vestnik MGSU. 2013. № 8. S. 97–103.
10. Lesovik V.S., Kucherov D.E. Klassifikatsiya aktivnykh mineral´nykh dobavok dlya kompozitsionnykh vyazhushchikh s uchetom genezisa. Vestnik BGTU im. V.G. Shukhova. 2012. № 3. S. 10–14.
11. Trunov P.V. Kompozitsionnye vyazhushchie s ispol´zovaniem vulkanogenno-osadochnykh porod Kamchatki i melkozernistye betony na ikh osnove //Dis... d.t.n., Belgorod. 2014, 161 c.
12. Danilin L.D., Drozhzhin V.S., Kuvaev M.D., Kulikov S.A., Maksimova N.V., Malinov V.I., Pikulin I.V., Redyushev S.A., Khovrin A.N. Polye mikrosfery iz zol- unosa - mnogofunktsional´nyy napolnitel´ kompozitsionnykh materialov. Tsement i ego primenenie. 2012. №4. S. 100–105.
13. Bazhenov Yu.M. Tekhnologiya betona //Izd., ASV. M., 2011, 524 c.
14. Voronin V.V. Effektivnye dobavki dlya vyazhushchikh veshchestv i betonov //Sovmestnyy mezhdunarodnyy nauchnyy simpozium «Nauchnye dostizheniya v issledovaniyakh o novykh sovremennykh stroitel´nykh materialakh». Khanoy. 2006. C. 98–105.
15. Bùi Danh Đại. Phụ gia khoáng hoạt tính cao cho bê tông chất lượng cao. Trường Đại học Xây Dựng - Hà Nội. 2010, tr.70. [Buy Dan´ Day. Vysokoaktivnye mineral´nye dobavki dlya polucheniya vysokokachestvennogo betona //Stroitel´nyy universitet. Khanoy. 2010, 70 c.].
16. Wanga A., Zhangb C., Suna W. Fly ash effects II. The active effect of fly ash. Cement and Concrete Research. 2004. Vol. 34. P. 2057–2060.
17. Tạ Ngọc Dũng, Nguyễn Văn Hoàn, Trần Tử Hùng, Nguyễn Thị Hoàn. Phụ gia siêu mịn cải thiện cường độ sớm của đá xi măng. Hội nghị Khoa học kỷ niệm 50 năm Viện KHCN Xây dựng, Hà Nội, 11-2013, Tr. 95-99. [Ta Ngok Zung, Nguen Van Khoan, Tran Khung Tu, Nguen Tkhi Khoan. Sverkhtonkie dobavki, povyshayushchie prochnost´ tsementnogo kamnya v rannem vozraste. Pyatidesyataya nauchnaya konferentsiya Instituta nauki i tekhnologii stroitel´stva. Khanoy, 11–2013, S. 95–99].