STRUCTURAL AND PHASE TRANSFORMATIONS IN THE FeO-SiO2 CaO-FeO I SYSTEM  AT INFLUENCE OF HIGH TEMPERATURES

R. N. Yastrebinskiy; Z. Pavlenko

doi:doi:10.12737/22714

STRUCTURAL AND PHASE TRANSFORMATIONS IN THE FeO-SiO2 CaO-FeO I SYSTEM AT INFLUENCE OF HIGH TEMPERATURES

Published в Bulletin of Belgorod State Technological University named after. V. G. Shukhov · Volume 1, Issue 12, 2016 · Pages 165–169 · Rubrics: Chemical technology

DOI 10.12737/22714

Received: 18.11.2016 Accepted: 18.11.2016 Published: 18.11.2016 Language of publication: RUS

Authors

R. N. Yastrebinskiy ¹ · Z. Pavlenko

1 Belgorod State Technological University named after V.G. Shukhov (docent)
Russian Federation

ABSTRACT

In work structural and phase transformations in two-component the iron oxides systems are considered at high-temperature influence, on the example of bivalent oxide of iron and oxides of calcium and silicon, by the being one of the main components of cement binding. Taking into account structure of a radiation protective composite ratios of FeO:CaO =2:1 and FeO:SiO2=4:1 are considered. Heat treatment of the FeO:CaO system in the recovery environment intensified dissociation of calcite and displaced her to the low temperatures area (from 700-1000 °C in the oxidizing environment to 600–800 °C) that is caused by influence of iron of various valency (first of all magnetite) on an ionic lattice of calcite. At 600 °C there is a formation of monocalcic ferrite. In process of enrichment of the СаО system in the range of 700–800 °C monocalcic ferrite passed into two-calcic. Formation of ferrite happens at continuous change of a valent and coordination condition of ions of iron and degree of an ionnost and covalence of a chemical bond of Fe-O in ferriferous complexes. In the FeO-SiO2 system it is established: modification transition of quartz in kristobalit began at 800 °C and intensively develops at 900 °C, against 1200 °C in oxidizing conditions; to modification transition of quartz in kristobalit formation of silicon dioxide with partially amorphous structure in the range of 600–700 °C consisting of ring structural elements from [SiO4] - tetrahedrons preceded.

KEYWORDS

iron oxides vyustit magnetite two-component systems calcium oxide silicon oxide thermal in-fluence structural and phase transformations

Information References

Authors:

1. Belgorod State Technological University named after V.G. Shukhov (docent)

Russian Federation

Type:

Article

Pages:

from 165 to 169

Status:

Published

Language:

Russian

Keywords:

iron oxides, vyustit, magnetite, two-component systems, calcium oxide, silicon oxide, thermal in-fluence, structural and phase transformations

References

1. Tret´yakov Yu.D. Tverdofazovye reaktsii. M.: Khimiya,1998, 359 s.

2. Khauffe K. Reaktsii v tverdykh telakh i na ikh poverkhnosti / M.: IL, 1982, 275 s.

3. Garner W. Chemistry of the solid state. London, Butterworth Sci Publ., 1985, p. 154.

4. Yastrebinskiy R.N., Bondarenko G.G., Pavlenko V.I. Oslablenie fotonnogo i neytronnogo izlucheniya zhelezo-magnetito-serpentinitovym radiatsionno-zashchitnym kompozitom. Perspektivnye materialy. 2016. № 10. S. 31-36.

5. Yastrebinskii R.N., Bondarenko G.G., Pavlenko V.I. Radiation resistance of structural radiation-protective composite material based on magnetite matrix. Inorganic Materials: Applied Research, 2016, Vol. 7, No. 5, pp. 718-723.

6. Rostovtsev S.T. Kinetika gazovogo vosstanovleniya oksidov zheleza i nekotorye vozmozhnosti intensifikatsii protsessa. Fizicheskaya khimiya okislov metallov. M.: Nauka, 1981, S. 42-47.

7. Leont´ev L.I., Chufarov G.I. O kinetike i mekhanizme vosstanovleniya ferritov kal´tsiya / /Zh.N.Kh. 1982. №1.S. 25-29.

8. Lazarev L.I. Kolebatel´nye spektry i stroenie silikatov. L.: Nauka, 1988, 348 s.

This work is licensed under Creative Commons Attribution 4.0 International

STRUCTURAL AND PHASE TRANSFORMATIONS IN THE FeO-SiO2 CaO-FeO I SYSTEM AT INFLUENCE OF HIGH TEMPERATURES

Confirmation

Регистрация