Zirconia dentures are gradually becoming a widespread type of dental prosthetics. The production of zirconia blanks for dentistry has been launched in our country. In recent years, the possibility of high-speed sintering of zirconia dentures has been well studied, which makes it possible to reduce the manufacturing process of dental restorations by four to five times. Zirconia ceramics compositions and high-speed sintering furnaces are being improved, sintering protocols are being optimized. In this paper, we reported about the influence of high-speed firing protocols on important material`s characteristic, such as three-point bend flexural strength and color parameters at ten different heating modes, differing by heating rates, final temperature and holding time during high-speed heat treatment of ceramic material. Accord-ing to the results of bending strength tests, samples obtained with a total time of high-speed firing from 20 to 60 minutes have similar values, more than 300 MPa. In accordance with the ISO 6872 standard, such flexural strength is sufficient for fabrication of single crowns in both the anterior and posterior groups of teeth. A study on the laboratory spectrophotometer (Spectron M) in the CIELab system, showed a multidirectional change in color characteristics at different heating rates and sintering temperatures. An increase in the value of zirconia sam-ples from domestic blanks "Ziceram T" produced by St. Petersburg firm "Zircon Ceramics" was established with a sufficient confidence grade. The shortened firing time leads to an in-crease in the value of the samples, which associate with a lower translucency.
translucent zirconia, express sintering, bending strength, color characteristics, sintering modes, chairside technique
1. Cokic S., Vleugels J., Van Meerbeek B., Camargo B., Willems E., Li M., Zhang F. Mechanical properties, aging stability and translucency of speed-sintered zirconia for chairside restorations // Dental Materials Journal 2020; 36, P. 959–972. https://doi.org/10.1016/j.dental.2020.04.026
2. Kaizer M.R., Gierthmuehlen P.C., Dos Santos M.B., Cava S.S., Zhang Y. Speed sintering translucent zirconia for chairside one-visit dental restorations: optical, mechanical, and wear characteristics.// Ceram Int 43, 2017, P. 999-1005. https://doi.org/10.1016/j.ceramint.2017.05.141
3. ISO/FDIS 6872 Dentistry — Ceramic materials
4. GOST R 58165-2018 (ISO/TR 28642:2016) Stomatologiya. Rukovodstvo po izmereniyam cveta
5. Luz J., Kaizer M., Ramos N., Thompson V., Anami L., Saavedra G., Zhang Y. Novel speed sintered zirconia by microwave technology // Dent Mater. – 2021;37(5):875- 878. https://doi.org/10.1016/j.dental.2021.02.026
6. Kaizer M.R., Gierthmuehlen P.C., Dos Santos M.B., Cava S.S., Zhang Y. Speed sintering translucent zirconia for chairside one-visit dental restorations: Optical, mechanical, and wear characteristics // Ceram Int. – 2017;1;43(14):10999-11005. doi:10.1016/j.ceramint.2017.05.141
7. Lebedenko I.Yu., D'yakonenko E.E., Sahabieva D.A., Llaka E. Prozrachnaya keramika na osnove dioksida cirkoniya dlya izgotovleniya monolitnyh zubnyh protezov. Obzor publikaciy v mezhdunarodnyh zhurnalah. Chast' 1. Stomatologiya. 2020;99;5:111-115. [I.Yu. Lebedenko, E.E. Dyakonenko, D.A. Sakhabieva, E. Llaka. Transparent ceramics based on zirconium dioxide for the manufacture of monolithic dentures. Review of publications in international journals. Part 1. Dentistry. 2020;99;5:111-115. (In Russ.)]. https://www.elibrary.ru/item.asp?id=44027968