The results of the investigations of susceptibility to hot cracks formation at welding of alloy 1151 in comparison with alloys 1201 and 1460 are shown. The character of alloy 1151 is a possibility of hot crack propagation both through a metal seam and through the area of a seam fusion with basic metal. The durability of welds of alloy 1151 carried out by fuse welding and friction welding with blending exceeds the durability of alloys 1201 and 1460. Corrosion resistance of welds of alloy 1151 exceeds considerably the corrosion resistance of compositions of alloy 1201.
argon-arc welding, friction welding with blending, wrought aluminum alloys, welds, welding wire, weldability, hot cracks, tests at increased temperatures, durability indices, stress corrosion.
1. Luzhnikov, L.P. Wrought Aluminum Alloys for Operation at Increased Temperatures. – М.: Metallurgy, 1965. – pp. 290.
2. Ovchinnikov, V.V., Manakov, I.N., Kurbatova, I.А. Weldability of castable alloy of VAL14 with wrought alloys 1151 and М40 // Blanking Production in Mechanical Engineering. – 2015.– №11. – pp. 7–12.
3. Ovchinnikov, V.V., Drits, А.М., Gureeva, М.А., Malov, D.V. Impact of grain size in initial structure of alloy 1565ch upon structure and properties of joints made by friction welding with blending // Electrometallurgy . – 2016. – №7. – pp. 17–26.
4. Ovchinnikov, V.V. High technologies of welding in manufacturing aluminum alloy transport objects // Science Intensive Technologies in Mechanical Engineering. – 2016. – №5(59). – pp.3–9.
5. Drits, А.М., Ovchinnikov, V.V. Results in weldability investigations of high-strength alloys of Al–Cu–Li–Mg system alloyed with silver, scandium, zirconium // Light Alloy Technology. – 2011. – №1. – pp. 29–38.
6. Procedure of Control МК 18-35–70. Tests of semi-products made of wrought aluminum and magnesium alloys for corrosion under stress at specified tensile load. – М.: VILS, 1970. – pp. 14.
7. SSR 9.019–74 (ISO–8591–89). Uniform System of Protection against Corrosion and Ageing. Aluminum and Magnesium Alloys. Methods of Rapid Corrosion Cracking Tests. – Introd. 01.01.75.